Product Description
ACS Aluminium clad steel conductor earth wire
Structure:
The conductor is composed by bare hard-drawn, round, aluminum clad steel wires of 14% to 40% IACS conductivity
Application:
It is widely used in aerial electricity transmission,overhead ground conductor, extra high voltage overhead conductor, optical fiber composite overhead ground line and self-danping conductor line,etc
Standard:
ASTM B416-98, AS1222, IEC61089
IF YOUR HAVE ANY INTERESTED PRODUCTS, PLS FEEL FREE TO CONTACT OUR SALES TEAM.
Approximate Properties of Hard-drawn 20.3% Conductivity Aluminum-Clad steel Wire (20.3%) |
|||||||||||||
Nominal Dia | Size | Calculated crosssectional area |
Min tensile strength |
Calculated breaking load |
Mincoating thickness |
D.C resistance at 20ºC≤ |
Weight |
||||||
in. | mm | AWG | mm2 | cmils | Mpa | psi | kn | mm | Ω/1000ft | Ω/km | kg/km | 1b/1000ft | |
0.2043 | 5.189 | 4 | 21.150 | 41740 | 1070 | 155000 | 22.60 | 0.259 | 1.222 | 4.009 | 139.32 | 93.63 | |
0.1880 | 4.775 | 4 | 17.908 | 35342 | 1100 | 160000 | 19.70 | 0.239 | 1.443 | 4.735 | 118.01 | 79.31 | |
0.1819 | 4.620 | 5 | 16.767 | 33090 | 1140 | 165000 | 18.10 | 0.231 | 1.541 | 5.056 | 110.48 | 74.25 | |
0.1729 | 4.392 | 5 | 15.150 | 29899 | 1170 | 170000 | 17.73 | 0.220 | 1.706 | 5.597 | 99.84 | 67.10 | |
0.1620 | 4.115 | 6 | 13.296 | 26240 | 1210 | 175000 | 16.00 | 0.206 | 1.943 | 6.375 | 87.61 | 58.88 | |
0.1549 | 3.934 | 6 | 12.155 | 23989 | 1240 | 180000 | 15.07 | 0.197 | 2.126 | 6.976 | 80.10 | 53.83 | |
0.1443 | 3,665 | 7 | 10.549 | 20820 | 1280 | 185000 | 13.50 | 0.183 | 2.450 | 8.038 | 69.47 | 46.69 | |
0.1369 | 3.477 | 7 | 9.495 | 18739 | 1310 | 190000 | 12.44 | 0.174 | 2.722 | 8.931 | 62.57 | 42.05 | |
0.1285 | 3.264 | 8 | 8.366 | 16510 | 1340 | 195000 | 11.20 | 0.163 | 3.089 | 10.135 | 55.15 | 37.03 | |
0.1144 | 2.906 | 9 | 6.633 | 13090 | 1340 | 195000 | 8.92 | 0.145 | 3.896 | 12.783 | 43.70 | 29.37 | |
0.1019 | 2.588 | 10 | 5.260 | 10380 | 1340 | 195000 | 7.07 | 0.129 | 4.912 | 16.116 | 34.66 | 23.29 | |
0.0907 | 2.304 | 11 | 4.170 | 8230 | 1340 | 195000 | 5.61 | 0.115 | 6.194 | 20.323 | 27.48 | 18.47 | |
0.0808 | 2.052 | 12 | 3.309 | 6530 | 1340 | 195000 | 4.45 | 0.103 | 7.811 | 25.628 | 21.80 | 14.65 |
Approximate Properties of Hard-drawn 27% Conductivity Aluminum-Clad steel Wire (27%) |
||||||||||||||
Nominal Dia | Size | Calculated cross sectional area | Min tensile strength |
Calculated breaking load |
Mincoating thickness |
D.C resistance at 20ºC≤ |
Weight |
|||||||
in. | mm | AWG | mm2 | cmils | Mpa | psi | kn | mm | Ω/1000ft | Ω/km | kg/km | 1b/1000ft | ||
0.2043 | 5.189 | 4 | 21.150 | 41740 | 862 | 125000 | 18.20 | 0.363 | 0.920 | 3.019 | 124.99 | 84.00 | ||
0.1880 | 4.775 | 4 | 17.908 | 35342 | 889 | 129000 | 15.92 | 0.334 | 1.087 | 3.566 | 105.83 | 71.12 | ||
0.1819 | 4.620 | 5 | 16.767 | 33090 | 917 | 133000 | 15.40 | 0.323 | 1.161 | 3.809 | 99.09 | 66.59 | ||
0.1729 | 4.392 | 5 | 15.150 | 29899 | 945 | 137000 | 14.32 | 0.307 | 1.285 | 4.215 | 89.54 | 60.17 | ||
0.1620 | 4.115 | 6 | 13.296 | 26240 | 972 | 141000 | 12.90 | 0.288 | 1.464 | 4.803 | 78.57 | 52.80 | ||
0.1549 | 3.934 | 6 | 12.155 | 23989 | 1000 | 145000 | 12.16 | 0.275 | 1.601 | 5.254 | 71.84 | 48.28 | ||
0.1443 | 3,665 | 7 | 10.549 | 20820 | 1034 | 150000 | 10.90 | 0.257 | 1.845 | 6.053 | 62.33 | 41.89 | ||
0.1369 | 3.477 | 7 | 9.495 | 18739 | 1062 | 154000 | 10.08 | 0.243 | 2.050 | 6.726 | 56.12 | 37.71 | ||
0.1285 | 3.264 | 8 | 8.366 | 16510 | 1076 | 156000 | 9.00 | 0.228 | 2.326 | 7.632 | 49.43 | 33.22 | ||
0.1144 | 2.906 | 9 | 6.633 | 13090 | 1076 | 156000 | 7.13 | 0.203 | 2.934 | 9.626 | 39.19 | 26.34 | ||
0.1019 | 2.588 | 10 | 5.260 | 10380 | 1076 | 156000 | 5.66 | 0.181 | 3.700 | 12.140 | 31.08 | 20.89 | ||
0.0907 | 2.304 | 11 | 4.170 | 8230 | 1076 | 156000 | 4.48 | 0.161 | 4.667 | 15.312 | 24.63 | 16.55 | ||
0.0808 | 2.052 | 12 | 3.309 | 6530 | 1076 | 156000 | 3.56 | 0.144 | 5.882 | 19.299 | 19.55 | 13.14 |
Approximate Properties of Hard-drawn 30% Conductivity Aluminum-Clad steel Wire (30%) |
||||||||||||||
Nominal Dia | Size | Calculated cross sectional area | Min tensile strength |
Calculated breaking load |
Mincoating thickness |
D.C resistance at 20ºC≤ |
Weight |
|||||||
in. | mm | AWG | mm2 | cmils | Mpa | psi | kn | mm | Ω/1000ft | Ω/km | kg/km | 1b/1000ft | ||
0.2043 | 5.189 | 4 | 21.150 | 41740 | 703 | 102000 | 14.90 | 0.389 | 0.828 | 2.717 | 118.64 | 79.73 | ||
0.1880 | 4.775 | 4 | 17.908 | 35342 | 731 | 106000 | 13.09 | 0.358 | 0.978 | 3.209 | 100.46 | 67.51 | ||
0.1819 | 4.620 | 5 | 16.767 | 33090 | 758 | 110000 | 12.70 | 0.347 | 1.045 | 3.429 | 94.06 | 63.21 | ||
0.1729 | 4.392 | 5 | 15.150 | 29899 | 786 | 114000 | 11.91 | 0.329 | 1.156 | 3.793 | 84.99 | 57.12 | ||
0.1620 | 4.115 | 6 | 13.296 | 26240 | 786 | 118000 | 10.50 | 0.309 | 1.317 | 4.321 | 74.59 | 50.13 | ||
0.1549 | 3.934 | 6 | 12.155 | 23989 | 814 | 122000 | 9.89 | 0.295 | 1.441 | 4.728 | 68.19 | 45.83 | ||
0.1443 | 3,665 | 7 | 10.549 | 20820 | 841 | 126000 | 8.87 | 0.275 | 1.660 | 5.446 | 59.18 | 39.77 | ||
0.1369 | 3.477 | 7 | 9.495 | 18739 | 869 | 128000 | 8.25 | 0.261 | 1.845 | 6.053 | 53.27 | 35.80 | ||
0.1285 | 3.264 | 8 | 8.366 | 16510 | 883 | 128000 | 7.38 | 0.245 | 2.094 | 6.870 | 46.95 | 31.55 | ||
0.1144 | 2.906 | 9 | 6.633 | 13090 | 883 | 128000 | 5.85 | 0.218 | 2.642 | 8.668 | 37.20 | 25.00 | ||
0.1019 | 2.588 | 10 | 5.260 | 10380 | 883 | 128000 | 4.47 | 0.194 | 3.329 | 10.922 | 29.52 | 19.84 | ||
0.0907 | 2.304 | 11 | 4.170 | 8230 | 883 | 128000 | 3.68 | 0.173 | 4.203 | 13.79 | 23.38 | 15.71 | ||
0.0808 | 2.052 | 12 | 3.309 | 6530 | 883 | 128000 | 2.92 | 0.154 | 5.295 | 17.373 | 18.57 | 12.48 |